Paste PVC

Features

Kaneka's paste PVC is one of its excellent products in Japan, based on the physical properties developed by our top proprietary technology and the outstanding processing capabilities as a resin. Used in a variety of fields, Kaneka has a complete line up of graded paste and blend resins and in order to meet the diverse demands of the market as well as advances in processing technology, Kaneka continues to carry out research into new product types.

Applications

Wallpapers, flooring, carpet
Electrical components, automobile components, different types of leather

  

詳細データ

Advantages

Paste PVC makes good use of unique processing methods, making it easy to form products high in added-value, so the benefits of using paste PVC continue to rise.

Lineup

■Granulated Products

Download of SDS

■Pulverized Products

List of Properties According to Grade

Granulated Products

High K Value Grade (PSH)
Grade K Value Paste Viscosity1)
(mPa/s)		 Volatile Content
(%)		 Bulk Density
(g/ml)		 Particle Size
150μm
on		 Properties2) Example Applications
PSH-180 77 3000 0.8 or less Approx. 0.50 10ppm or less Low viscosity, low water absorbancy
Greater electrical resistance		 Regular, body sealer
Electrical components
PSH-161 77 3000 0.8 or less Approx. 0.50 10ppm or less Low viscosity, good for foam-forming cells
Good sol defoaming properties		 PVC steel plate
Chemically embossed wallpaper
PSH-261 75 4500 0.8 or less Approx. 0.50 10ppm or less Good sol defoaming properties
Low humidity absorbency, greater electrical resistance		 Electrical components
PSH-247 77 3500 0.8 or less Approx. 0.50 10ppm or less Good sol defoaming properties
Low H.S. viscosity		 Mesh sailcloth
(Cap seals)
PSH-985 94 2500 0.8 or less Approx. 0.50 10ppm or less Low viscosity, high physicality
Low luster, low water absorbency		 Flooring top coat
PSH-945 - 3000 0.8 or less Approx. 0.50 10ppm or less Mat effect Flooring top coat
Wallpaper base coat
PSH-947 - 3500 0.8 or less Approx. 0.50 10ppm or less Mat effect Flooring top coat
Wallpaper base coat
Mid K Value Grade (PSM)
Grade K Value Paste Viscosity1)
(mPa/s)		 Volatile Content
(%)		 Bulk Density
(g/ml)		 Particle Size
150μm
on		 Properties2) Example Applications
PSM-154 71 3500 0.8 or less Approx. 0.50 10ppm or less Good foam-forming properties
Good chemical embossing properties		 Flooring material foam layer
PSM-162 70 3000 0.8 or less Approx. 0.50 10ppm or less Good foam-forming properties
Good chemical embossing properties		 Flooring material foam layer
PSM-176 72 3000 0.8 or less Approx. 0.50 10ppm or less Low sol viscosity
Suitable for stable storage		 Tile carpet
Low K Value Grade (PSL)
Grade K Value Paste Viscosity1)
(mPa/s)		 Volatile Content
(%)		 Bulk Density
(g/ml)		 Particle Size
150μm
on		 Properties2) Example Applications
PSL-180 66 3000 0.8 or less Approx. 0.50 10ppm or less Low L.S. viscosity, low water absorbancy
Foam forming able to produce foam independently)		 Body sealer
Flooring material foam layer
PSL-675 60 3000 0.8 or less Approx. 0.50 10ppm or less Low L.S. viscosity, low H.S. viscosity
Appropriate for use as high filler and high foam forming		 Wallpapers
PSL-685 64 7000 0.8 or less Approx. 0.50 10ppm or less High H.S. viscosity, good for foam-forming cells
High performance in preventing cell bond and making surface scaling when emboss processing		 Wallpapers
Vinyl Acetate Copolymer Grade
Grade K Value Paste Viscosity1)
(mPa/s)		 Volatile Content
(%)		 Bulk Density
(g/ml)		 Particle Size
150μm
on		 Properties2) Example Applications
PCH-175 76 4000 1.0 or less Approx. 0.50 10ppm or less Low viscosity, suitable for stable storage
Good gelatinization properties, VAc: 5%		 Tile carpet
PCH-843 80 2000* 1.0 or less Approx. 0.50 10ppm or less Good gelatinization properties, high physical properties
Suitable for stable storage, VAc: 8%		 Body sealer, under body coat

1): Paste viscosity is typical values measured and recorded in accordance with JIS K7383 and K7117-1.
In terms of composition, the basic ratio is 100 of polymer resin with 60 of the plasticizing agent (DOP).
Values marked with an asterisk have a plasticizing agent value of 100.
Paste viscosity can change with compounding and usage conditions.

2): LS viscosity = Low Share viscosity; HS viscosity = High Share viscosity; VAc = Vinyl Acetate

Pulverized Products

High K Value Grade (PSH)
Grade K Value Paste Viscosity1)
(mPa/s)		 Volatile Content
(%)		 Bulk Density
(g/ml)		 Particle Size
150μm
on		 Properties2) Example Applications
PSH-10 75 3000 0.8 or less Approx. 0.30 10ppm or less Low viscosity, low water absorbency
Greater electrical resistance		 Regular, body sealer
Toys, electrical components
PSH-31 77 3000 0.8 or less Approx. 0.30 10ppm or less Low viscosity, good for foam-forming cells
Good sol defoaming properties		 PVC steel plate
Chemically embossed wallpaper
PSH-24 87 2500 0.8 or less Approx. 0.30 10ppm or less High physical properties
Good resistance to draw-down		 Leathers for automobile use
Mid K Value Grade (PSM)
Grade K Value Paste Viscosity1)
(mPa/s)		 Volatile Content
(%)		 Bulk Density
(g/ml)		 Particle Size
150μm
on		 Properties2) Example Applications
PSM-30 72 3000* 0.8 or less Approx. 0.30 10ppm or less Good sol defoaming properties
Good properties for resisting gumming up		 Sailcloth, gloves
PSM-31 72 3500 0.8 or less Approx. 0.30 10ppm or less Good sol defoaming properties
Low viscosity, good foam-forming properties		 Cellular leathers, sol
PSM-271R 69 9000 0.8 or less Approx. 0.30 10ppm or less Low H.S. viscosity, high thixotropy
Good foam-forming properties		 Rotary screen method wallpaper
Low K Value Grade (PSL)
Grade K Value Paste Viscosity1)
(mPa/s)		 Volatile Content
(%)		 Bulk Density
(g/ml)		 Particle Size
150μm
on		 Properties2) Example Applications
PSL-31 66 3000 0.8 or less Approx. 0.30 10ppm or less Good foam-forming properties (continuous foam) Wallpapers
Flooring material foam layer
PSL-275 60 3000 0.8 or less Approx. 0.30 10ppm or less Low L.S. viscosity, low H.S. viscosity
Appropriate for use as high filler and high foam forming		 Wallpapers
PSL-290R 64 14000 0.8 or less Approx. 0.30 10ppm or less Low H.S. viscosity, high thixotropy
Good for foam-forming cells		 Rotary screen method wallpaper
Vinyl Acetate Copolymer Grade
Grade K Value Paste Viscosity1)
(mPa/s)		 Volatile Content
(%)		 Bulk Density
(g/ml)		 Particle Size
150μm
on		 Properties2) Example Applications
PCH-12 74 3500 1.0 or less Approx. 0.30 10ppm or less Low viscosity, good gelatinization properties
VAc: 5%		 Body sealer
Under body coat
PCH-72 80 2000* 1.0 or less Approx. 0.30 10ppm or less Good gelatinization properties, high physical properties
Suitable for stable storage, VAc: 8%		 Body sealer
Under body coat
Blend Resin Grade (PBM) (Reduced viscosity type)
Grade K Value Paste Viscosity1)
(mPa/s)		 Volatile Content
(%)		 Bulk Density
(g/ml)		 Particle Size
150μm
on		 Properties2) Example Applications
PBM-6 66 0.6 or less Approx. 0.45 2 ppm or less Approx. 36 Good gelatinization properties
VAc: 3%		 Body sealer, under body coat
PBM-B5F 68 0.4 or less Approx. 0.55 2 ppm or less Approx. 40 Reduced viscosity, greater mat effect
High physical properties		 Flooring, wallpapers
PS-300K 69 0.4 or less Approx. 0.36 2 ppm or less Approx. 26 Good rotary screen characteristics Rotary screen method wallpaper
XPS-300L - 0.4 or less Approx. 0.36 2 ppm or less Approx. 26 Good rotary screen characteristics
Greater mat effect		 Rotary screen method wallpaper

1): Paste viscosity is typical values measured and recorded in accordance with JIS K7383 and K7117-1.
In terms of composition, the basic ratio is 100 of polymer resin with 60 of the plasticizing agent (DOP).
Values marked with an asterisk have a plasticizing agent value of 100.
Paste viscosity can change with compounding and usage conditions.

2): LS viscosity = Low Share viscosity; HS viscosity = High Share viscosity; VAc = Vinyl Acetate

Products of Overseas Groupe Company